14Mpa
Fiber Optical Plastic Protect Sleeve
  |
Specification
1) Hot melt adhesive 2) Heat shrinkable polyolefin 3) Stainless steel needle
|
Specifications:
Shrinking Temperature (°C) | 110 ~ 130 |
Radial Shrinking Rate (%) | >50 |
Axial Shrinking Rate (%) | <10 |
Low Temperature Property | No crackle at -55°C lasting 4 hours |
Normal Operation Temperature (°C) | -55°C ~ + 135°C |
Normal Operature Relative Humidity | ≤95% |
Spark- over Strength (kV/mm) | ≥20 |
Tensile Strength (Mpa) | 20 |
Loss at -40°C | 0.03dB |
Loss at +60°C RH95% | 0.02dB |
Standard (for Ribbon 45mm Length):
Type | 4~6 fiber Single Ceramic Bar | 4~6 fiber Double Ceramic Bar | 8~12 fiber Single Ceramic Bar | 8~12 fiber Double Ceramic Bar | |
Outer Tube | Outer Diameter | 4.4±0.1 | 4.8±0.1 | 5.8±0.1 | 5.8±0.1 |
Thickness | 0.2±0.05 | 0.2±0.05 | 0.25±0.05 | 0.25±0.05 | |
Length | 42.0±1 | 42.0±1 | 42.0±1 | 42.0±1 | |
Material | Flexible Polyolefin | Flexible Polyolefin | Flexible Polyolefin | Flexible Polyolefin | |
Inner Tube | Inner Diameter | 2.6 x 1.6±0.1 | 2.6 x 1.6±0.1 | 3.5 x 2.2±0.1 | 3.5 x 2.2±0.1 |
Length | 0.3±0.1 | 0.3±0.1 | 0.5±0.1 | 0.5±0.1 | |
Thickness | 40.0±1 | 40.0±1 | 40.0±1 | 40.0±1 | |
Material | EVA | EVA | EVA | WVA | |
Ceramic Bar | Diameter | 3.0±0.2 | 3.0±0.2 | 4.0±0.2 | 4.0±0.2 |
Length | 40.0±0.5 | 40.0±0.5 | 40.0±0.5 | 40.0±0.5 | |
Amount | 1 | 2 | 1 | 2 | |
Material | 95 Ceramic | 95 Ceramic | 95 Ceramic |
| |
/p>
| Q1: Are you a manufacturer or a trading company? |
| A: We are a manufacturer, providing OEM & ODM service. |
| Q2. Are your products conforming to our standards? |
| A: Our products can pass the testing as you require, e.g.: CE, RoHS, etc. |
| Q3. What’s the warranty for your products? |
| A: Normally it is 2 years. |
| Q4. What is the delivery date for a sample? |
| A: About the 3-4 working days after getting payment. |
| Q5. What about after-sale service? |
| A: 24hours online, we have professional after-sale department. Any problem, just contact us. |
If you need any more information or have any enquiries,
Please Click Here.